¡¡¡¡¡¡¡¡¡¡¡¡¡¡TECHNICAL
ANALYSIS 1
PHYSIAL PROPERTIES |
|
Grade |
AX¡ª100# |
Color |
Pallide-flavens-pink |
Description |
Calcined |
Specific Gravity £¬ g/cm3 |
2.1-2.3 |
Moisture |
¡Ü 1% |
PH |
6.5-8.0 |
Bulk Density £¬ g/cm3 |
0.34-0.42 |
Flow Rate Darey |
0.08-0.36 |
Water Absorption £¬ %by weight |
180 |
Oil Absorption £¬ %by weight |
160 |
Median Partile Size |
6---15 |
CHEMICAL PROPERTIES Weight% |
|
Sio2 |
¡Ý 87.6% |
Al2O3 |
¡Ü 2.5%
|
Fe2O3 |
¡Ü 1.50%
|
CaO |
¡Ü 0.5%
|
MgO |
¡Ü 0.5%
|
Loss On Lgnition |
¡Ü 1.0%
|
¡¡¡¡¡¡¡¡¡¡¡¡¡¡TECHNICAL ANALYSIS
2
PHYSIAL PROPERTIES |
|
Grade |
AX¡ª700# |
Color |
White |
Description |
Flux Calcined |
Specific Gravity £¬ g/cm3 |
2.1-2.3 |
Moisture |
¡Ü 2.0% |
PH |
7-10 |
Bulk Density £¬ g/cm3 |
0.36-0.42 |
Flow Rate Darey |
2.2-2.9 |
Water Absorption £¬ %by weight |
180 |
Oil Absorption £¬ %by weight |
160 |
Median Partile Size |
10---20 |
CHEMICAL PROPERTIES Weight% |
|
Sio2 |
¡Ý 87.6% |
Al2O3 |
¡Ü 2.5% |
Fe2O3 |
¡Ü 1.50% |
CaO |
¡Ü 0.5% |
MgO |
¡Ü 0.5% |
Loss On Lgnition |
¡Ü 1.0% |
¡¡¡¡¡¡¡¡¡¡¡¡¡¡TECHNICAL ANALYSIS
3
PHYSIAL PROPERTIES |
|
Grade |
AX¡ª800# |
Color |
White |
Description |
Flux Calcined |
Specific Gravity £¬ g/cm3 |
2.1-2.3 |
Moisture |
¡Ü 2.0% |
PH |
7-10 |
Bulk Density £¬ g/cm3 |
0.38-0.42 |
Flow Rate Darey |
2.9-4.9 |
Water Absorption £¬ %by weight |
180 |
Oil Absorption £¬ %by weight |
160 |
Median Partile Size |
15---25 |
CHEMICAL PROPERTIES Weight% |
|
Sio2 |
¡Ý 87.6% |
Al2O3 |
¡Ü 2.5% |
Fe2O3 |
¡Ü 1.50% |
CaO |
¡Ü 0.5% |
MgO |
¡Ü 0.5% |
Loss On Lgnition |
¡Ü 1.0% |
¡¡¡¡¡¡¡¡¡¡¡¡¡¡TECHNICAL ANALYSIS 4
PHYSIAL PROPERTIES |
|
Grade |
AX¡ª900# |
Color |
White |
Description |
Flux Calcined |
Specific Gravity £¬ g/cm3 |
2.1-2.3 |
Moisture |
¡Ü 0.8% |
PH |
7-10 |
Bulk Density £¬ g/cm3 |
0.38-0.42 |
Flow Rate Darey |
5-6 |
Water Absorption £¬ %by weight |
180 |
Oil Absorption £¬ %by weight |
160 |
Median Partile Size |
20---25 |
CHEMICAL PROPERTIES Weight% |
|
Sio2 |
¡Ý 87.6% |
Al2O3 |
¡Ü 2.5% |
Fe2O3 |
¡Ü 1.50% |
CaO |
¡Ü 0.5% |
MgO |
¡Ü 0.5% |
Loss On Lgnition |
¡Ü 1.0% |
¡¡¡¡¡¡¡¡¡¡TECHNICAL ANALYSIS 5
PHYSIAL PROPERTIES |
|
Grade |
AX¡ª1000# |
Color |
White |
Description |
Flux Calcined |
Specific Gravity £¬ g/cm3 |
2.1-2.3 |
Moisture |
¡Ü 0.8% |
PH |
7-10 |
Bulk Density £¬ g/cm3 |
0.38-0.42 |
Flow Rate Darey |
6-10 |
Water Absorption £¬ %by weight |
180 |
Oil Absorption £¬ %by weight |
160 |
Median Partile Size |
20---30 |
CHEMICAL PROPERTIES Weight% |
|
Sio2 |
¡Ý 87.6% |
Al2O3 |
¡Ü 2.5% |
Fe2O3 |
¡Ü 1.50% |
CaO |
¡Ü 0.5% |
MgO |
¡Ü 0.5% |
Loss On Lgnition |
¡Ü 1.0% |
¡¡¡¡¡¡¡¡¡¡TECHNICAL ANALYSIS 6
PHYSIAL PROPERTIES |
|
Grade |
AX¡ª3000# |
Color |
White |
Description |
Flux Calcined |
Specific Gravity £¬ g/cm3 |
2.1-2.3 |
Moisture |
¡Ü 0.8% |
PH |
7-10 |
Bulk Density £¬ g/cm3 |
0.38-0.42 |
Flow Rate Darey |
>10 |
Water Absorption £¬ %by weight |
180 |
Oil Absorption £¬ %by weight |
160 |
Median Partile Size |
30---50 |
CHEMICAL PROPERTIES Weight% |
|
Sio2 |
¡Ý 87.6% |
Al2O3 |
¡Ü 2.5% |
Fe2O3 |
¡Ü 1.50% |
CaO |
¡Ü 0.5% |
MgO |
¡Ü 0.5% |
Loss On Lgnition |
¡Ü 1.0% |
|
|